TGIC Based Polyester Resin For Outdoor Powder Coatings |
Product Description: ZJ9037 is a kind of saturated carboxyl polyester resin, mixed with TGIC in 93/7 polyester/TGIC for exterior environment powder coatings
Product Properties: Excellent overall performance, High cross-linking density, fast reaction/curing speed, excellent weather resistance, gloss retention > 90% . Especially suitable for Architectural and Aluminum profile .
Specifications:
Performance |
Specifications |
Appearance |
Light color flake solid |
Color(50%DMF) |
≤3 |
Acid Value(mgKOH/g) |
30-36 |
Softening Point (ball) (ºC) |
108~120 |
Glass Transition Temp /Tg(ºC) |
64 |
Viscosity(P/200ºC) |
60~80 |
Starting Formulation:
Material |
ZJ9037 |
TGIC |
Pigment & Filler |
Flow Agent(PV5) |
Benzoin |
Formula |
530g |
40g |
416g |
9g |
5g |
Extrusion Condition: Casing setting temperature: |
125~135ºC |
R.P.m: |
200~300rpm |
Particle size: |
<100μm |
Execution Condition: |
|
Spraying tension: |
60~80KV |
Thickness: |
60~80μm |
Curing Condition: |
200ºC/10min(MT) |
Properties: |
|
Gloss(60°): |
≥90%; |
Bending(φ1mm): |
PASS; |
Adhesion(grid1mm): |
0~1mm; |
Hardness(pencil) : |
≥1H; |
Impact(50kg·cm): |
PASS |
Package |
25kgs/kraft paper-PP woven compound bag |
Product Picture ---ZJ9037 |
Huangshan Zhengjie New Materials Co.,Ltd is a high-tech enterprise specializing in R&D, production and marketing of polyester resin & primid (HAA) curing agent for powder coatings in Anhui China .
At present, the annual output value of the company is nearly 500 million RMB ,with registered trademarks and more than 25 independent patents . The "Zhengjie" brand polyester resin and primid (HAA) curing agent are highly recognized by customers, and the products are exported to all over the world.
TGIC Based Polyester Resins For Powder Coating
Primid(HAA) Based Polyester Resins For Powder Coating
Hybrid Polyester Resins for Epoxy Resin Cure (50:50)
Hybrid Polyester Resins for Epoxy Resin Cure(60:40)
Hybrid Polyester Resins for Epoxy Resin Cure(70:30)
ZJ552 Curing Agent Primid(HAA)